Under the spread of the new crown epidemic, after Americans experienced life and death, they set off the largest "resignation wave" in history, and the number of resignations broke the highest record since statistics began in 2000. Since April this year, more than 4 million people in the United States have voluntarily resigned each month. In August, the number of resignations exceeded 4.27 million, and in November, it rose to 4.4 million. The operation of society is linked. The large number of departures in the United States has led to a large shortage of labor; and the shortage of a large number of labor has directly led to the supply chain crisis in the United States; the supply chain crisis has directly affected prices and prices in the United States. The economy has a direct effect on people's lives.
The economic downturn will affect the market demand for graphite anode .
Graphite anode material is the main raw material of lithium ion battery anode sheet. Due to its rough processing technology, late start and industry specificity, the product is prone to quality problems such as fiber foreign matter and fine powder. The influencing factors, failure modes and control methods of these two quality problems are explained one by one below.
The proportion of fine powder of graphite anode also seriously affects the processing technology of the battery factory. When the fine powder in the graphite negative electrode is higher than a certain ratio, the appearance of the produced negative electrode sheet may also have many small particles and scratches, resulting in the scrapping of the negative electrode sheet.
The fine powder level of the graphite negative electrode is closely related to the process before graphitization and graphitization, and the fine powder that has been produced can be screened by a jet pulverization grading system.
After the graphitization, the powder collides in the airflow device, and the collided powder becomes smaller. Under a certain airflow, the fine powder is blown out of the device and enters the fine powder collecting device, and the airflow through the adjusting device can be different. The graphite negative electrode of the particle size is sorted out, and the powder in the fine powder collecting device is removed, thereby obtaining a graphite negative electrode product whose fine powder level satisfies the customer's demand.
Fiber foreign matter
The metal foreign matter in the graphite anode powder and other visible foreign objects have been widely concerned. The anode manufacturing industry also controls the foreign matter in different stages of the manufacturing process according to the characteristics of foreign materials.
However, fiber foreign matter is a foreign object that is easily overlooked by everyone, and its influence on battery safety performance is increasing. When the amount of fibrous foreign matter reaches a certain level or accumulates in the powder, the appearance of the negative electrode sheet after coating is uneven, and electron beam and elemental analysis are performed on the uneven spots, and it is confirmed that the composition of the uneven spots is fiber.
The concave and convex points were observed under a microscope, and it was found that the fibrous foreign matter occupied the position of the negative electrode powder, and the amount of the negative electrode coating in this portion was reduced, thereby causing a lithium-inducing problem in the charging and discharging process of the battery, causing the explosion of the lithium ion battery.
Therefore, the quality control of fiber foreign matter is imperative. By testing the powders in each process, it was found that the negative electrode powder packaging bags used in each process were the main source of fibrous foreign materials.
Since the temperature of graphitization is high, the fiber can be carbonized, and the carbonized fiber can be turned into fine slag through the vibrating screen, and is present in the powder in the form of powder, which does not cause appearance quality problems on the pole piece, so The control of the fibrous material mainly manages the process after the graphitization.
After the graphitization process, a ton bag of fiber material is used in the turnover of the graphite negative electrode, which will rub with the equipment during transportation and feeding, thereby causing the fiber to fall off, and after the fiber is detached, it is easy to and the graphite negative electrode powder. The flow is transferred to the sieving process, and the fibers are sprinkled into the powder through the mesh of the screen after the powder is shaken for several hours on the screen of the vibrating screen.
To control the amount of fiber, firstly protect the foreign material of the ton bag of fiber material, add a layer of plastic bag protection in the ton bag, or replace the ton bag with a plastic bucket. At the feeding port, a large-diameter screen is added to intercept the large bundle of fiber ropes, and the inlet of the feeding equipment is cuffed to prevent the equipment from scratching the bag and causing fiber problems.
Since the beginning of this year, China's macro policies have made continuous efforts to stabilize economic growth. America and Europe are raising interest rates to control inflation. On March the European Central Bank left its three key interest rates unchanged and began to scale back its asset-purchase programme. Then the Federal Reserve raised the target range of the federal funds rate by 25 basis points to 0.25%-0.5%. The accelerated tightening of monetary policies in the US and Europe pushed capital back to the US and increased interest rates, which will definitely increase the risk of RMB depreciation and capital outflow. The price and market of the graphite anode will also be affected, resulting in a range of fluctuations. You are welcome to contact us for the latest quotation of graphite anode .
Water-based zinc stearate mainly uses zinc stearate special additives, sandpaper polishing paint, thermal paper sensitizer functional additives, rubber and water-based paint release agents, etc.…
Erbium oxide Er2O3 powder is a pink powder with the chemical formula Er2O3, mainly used as an additive for yttrium iron garnet and a control material for nuclear reactors.…
Iron disilicide is an inorganic silicon compound with a molecular formula of FeSi2 and a molecular weight of 119.975. It is a gray powder, odorless, tetragonal crystals. For hydrogen catalytic oxidation and methanation catalyst.…